焊材特性
*焊后细化的碳化物均匀的分布在强化的基体内具有高抗磨性
*具有高抗磨性，产生奥氏体，堆焊材料中含初始碳化物
*工件表面堆焊后，再变形性有限
*材料不能机械加工处理
*应用温度范围不超过550℃
焊材应用
适用于对承受高度磨损和中等冲击的部件作硬面处理，例如堆焊再制造电厂磨煤辊/盘瓦、水泥厂立磨磨辊/盘、矿山粉碎机辊、破碎机锤，制造耐磨复合钢板，复合辊堆焊等。
参照标准：BS EN14700:2005
规格： Φ2.0mm、Φ2.4mm、Φ2.8mm、Φ3.2mm
包装： 卷装25 kg/卷、50kg/卷；桶装200kg/桶
焊接指示： 不用加惰性气体；交直流两用；电弧要尽可能短
|
Bezeichnung |
Schlackentyp |
EN |
AWS |
|
MEGAFIL©710M |
Metal powder |
T 46 6 MM 1 H 5 |
E 70 C-6M H4 |
|
MEGAFIL©235M |
Metal powder |
T Mo1 M M 1 H5 |
E 80 C-D2-H4 |
|
MEGAFIL©236M |
Metal powder |
T CrMo1 M M 1 H5 |
E 80 C-B2 H4 |
|
MEGAFIL©240M |
Metal powder |
T 50 6 Ni M M 1H5 |
E 80 C-Ni1 H4 |
|
MEGAFIL©281M |
Metal powder |
T 46 4Z MM 1 H 5 |
E 80 C-G H4 |
|
MEGAFIL©741M |
Metal powder |
T 55 6 1NiMo B M 2 H5 |
E 90 C-K3M H4 |
|
MEGAFIL©940M |
Metal powder |
T 55 6 Mn1, 5Ni M M 1 H5 |
E 80 C-Ni2 H4 |
|
MEGAFIL©250M |
Metal powder |
T 69 6 Mn2, 5Ni M M 1 H5 |
E 80 C-Ni3 H4 |
|
MEGAFIL©742M |
Metal powder |
T 69 6 Mn2NiCrMo M M 1 H5 |
E 110 C-K4 H4 |
|
MEGAFIL©807M |
Metal powder |
T 89 0 Z M M 1 H5 |
E 120 C-K4 H4 |
|
MEGAFIL©1100M |
Metal powder |
T 89 4 Mn2NiCrMo M M 1 H5 |
E 120 C-K4 H4 |
|
MEGAFIL©713R |
rutile |
T 46 4(2) P M(C) 1 H5 |
E 71 T-1 M H4 |
|
MEGAFIL©781R |
rutile |
T 46 2 Z P M(C) 1 H5 |
E 81 T1-G H4 |
|
MEGAFIL©821R |
rutile |
T50(46)6(4)1Ni P M(C)1 H5 |
E 81 T1-Ni1 H4 |
|
MEGAFIL©822R |
rutile |
T46(50)4(6)1Ni P M(C)1 H5 |
E 81 T1-Ni1 H4 |
|
MEGAFIL©825R |
rutile |
T Mo P M1 H5 |
E 81 T1-A1M H4 |
|
MEGAFIL©836R |
rutile |
T CrMo 1 P M 1 H5 |
E 81 T1-B2 H4 |
|
MEGAFIL©731B |
rutile |
T 46 4 B M(C) 3 H5 |
E 70 T-5M H4 |
|
MEGAFIL©735B |
rutile |
T Mo B M3 H5 |
E 80 T5-A1M H4 |
|
MEGAFIL©736B |
rutile |
T CrMo1 B M 3 H5 |
E 80T5-B2 H4 |
|
MEGAFIL©737B |
rutile |
T CrMo2 B M 3 H5 |
E 80T5-B3 H4 |
|
MEGAFIL©838B |
rutile |
T CrMo1 B M 3 H5 |
E 80T5-B2 H4 |
|
MEGAFIL©741B |
rutile |
T 55 6 1NiMo B M(C) 3 H5 |
E 80 T5-K2M H4 |
|
MEGAFIL©742B |
rutile |
T 69 6 Mn2NiCrMo B M 3 H5 |
E 110 T5-K4M H4 |
|
MEGAFIL©745B |
rutile |
T 89 4 Mn2NiCrMo B M 3 H5 |
E 120 T5-K4M H4 |
|
MEGAFIL©807B |
rutile |
T 89 0 Z B M 3 H5 |
E 120 T5-K4M H4 |