牌号 |
AWS |
熔敷金属化学成分(%) |
熔敷金属力学性能 |
用 途 |
|
C |
Mn |
Si |
S |
P |
Cr |
Ni |
Mo |
Cu |
其它 |
R m
(MPa) |
A
(%) |
|
E5MoV-15 |
— |
≤0.12
0.074 |
0.5-0.9
0.68 |
≤0.50
0.42 |
≤0.030
0.010 |
≤0.030
0.019 |
4.5-6.0
5.3 |
— |
0.40-0.70
0.55 |
≤0.5
0.052 |
V : 0.10-0.35
0.25 |
≥540
625
(750℃×4h) |
≥14
20
(750℃×4h) |
用于Cr5MoV等珠光体耐热钢的焊接 |
|
E410-15 |
E410-15 |
≤0.12
0.048 |
≤1.0
0.81 |
≤0.90
0.44 |
≤0.030
0.007 |
≤0.030
0.023 |
11.0-13.5
13.16 |
≤0.70
0.51 |
≤0.75
0.12 |
≤0.75
0.15 |
— |
≥450
545
(750℃×1h) |
≥20
23
(750℃×1h) |
用于0Cr13、1Cr13钢和耐磨耐蚀钢的表面堆焊 |
|
E410NiMo-15 |
E410NiMo-15 |
≤0.06
0.030 |
≤1.0
0.71 |
≤0.90
0.26 |
≤0.030
0.006 |
≤0.030
0.016 |
11.0-12.5
12.15 |
4.0-5.0
4.39 |
0.40-0.70
0.45 |
≤0.75
0.17 |
— |
≥760
890
(610℃×1h) |
≥15
17
(610℃×1h) |
用于0Cr13不锈钢焊接 |
|
E308-16 |
E308-16 |
≤0.08
0.052 |
0.5-2.5
1.33 |
≤0.90
0.71 |
≤0.030
0.007 |
≤0.030
0.021 |
18.0-21.0
19.82 |
9.0-11.0
9.45 |
≤0.75
0.13 |
≤0.75
0.20 |
— |
≥550
630 |
≥35
40 |
用于工作温度低于300℃的0Cr19Ni9不锈钢结构的焊接 |
|
E308-15 |
E308-15 |
≤0.08
0.057 |
0.5-2.5
1.35 |
≤0.90
0.41 |
≤0.030
0.007 |
≤0.030
0.021 |
18.0-21.0
19.78 |
9.0-11.0
9.75 |
≤0.75
0.15 |
≤0.75
0.20 |
— |
≥550
630 |
≥35
40 |
用于工作温度低于300℃的0Cr19Ni9不锈钢结构的焊接 |
|
E308H-16 |
E308H-16 |
0.04-0.08
0.058 |
0.5-2.5
1.14 |
≤0.90
0.62 |
≤0.030
0.007 |
≤0.030
0.020 |
18.0-21.0
19.70 |
9.0-11.0
9.68 |
≤0.75
0.20 |
≤0.75
0.10 |
— |
≥550
645 |
≥35
42 |
用于工作温度低于300℃的0Cr19Ni9不锈钢结构的焊接 |
|
E308L-16 |
E308L-16 |
≤0.04
0.028 |
0.5-2.5
1.15 |
≤0.90
0.70 |
≤0.030
0.010 |
≤0.030
0.019 |
18.0-21.0
19.25 |
9.0-11.0
9.49 |
≤0.75
0.10 |
≤0.75
0.13 |
— |
≥520
590 |
≥35
44 |
用于超低碳00Cr19Ni10或0Cr18Ni10Ti不锈钢的焊接 |
|
E308L-16W |
E308L-16 |
≤0.04
0.029 |
0.5-2.5
2.14 |
≤0.90
0.53 |
≤0.030
0.010 |
≤0.030
0.019 |
18.0-21.0
19.25 |
9.0-11.0
10.2 |
≤0.75
0.10 |
≤0.75
0.13 |
— |
≥520
590 |
≥35
44
-196℃
A KV 41(J) |
用于超低碳00Cr19Ni10或0Cr18Ni10Ti不锈钢的焊接,在196℃下有良好的韧性，适用于LNG储罐及管道的焊接。 |
|
E309-16 |
E309-16 |
≤0.15
0.068 |
0.5-2.5
1.15 |
≤0.90
0.62 |
≤0.030
0.011 |
≤0.030
0.026 |
22.0-25.0
24.44 |
12.0-14.0
12.42 |
≤0.75
0.19 |
≤0.75
0.20 |
— |
≥550
635 |
≥25
33 |
同类型不锈钢及异种钢的焊接 |
|
E309-15 |
E309-15 |
≤0.15
0.070 |
0.5-2.5
1.21 |
≤0.90
0.52 |
≤0.030
0.009 |
≤0.030
0.021 |
22.0-25.0
24.15 |
12.0-14.0
12.60 |
≤0.75
0.13 |
≤0.75
0.11 |
— |
≥550
620 |
≥25
35 |
同类型不锈钢及异种钢的焊接 |
|
E309Mo-16 |
E309Mo-16 |
≤0.12
0.053 |
0.5-2.5
1.22 |
≤0.90
0.63 |
≤0.030
0.012 |
≤0.030
0.023 |
22.0-25.0
23.53 |
12.0-14.0
13.46 |
2.0-3.0
2.24 |
≤0.75
0.20 |
— |
≥550
645 |
≥25
35 |
用于耐硫酸介质腐蚀的同类型不锈钢焊接及异种钢的焊接 |
|
E309MoL-16 |
E309MoL-16 |
≤0.04
0.029 |
0.5-2.5
1.05 |
≤0.90
0.54 |
≤0.030
0.009 |
≤0.030
0.021 |
22.0-25.0
23.23 |
12.0-14.0
12.65 |
2.0-3.0
2.21 |
≤0.75
0.15 |
— |
≥540
630 |
≥25
34 |
用于相同类型的超低碳不锈钢材料（如尿素合成塔衬里）及异种钢焊接 |
|
E309L-16 |
E309L-16 |
≤0.04
0.033 |
0.5-2.5
1.23 |
≤0.90
0.65 |
≤0.030
0.009 |
≤0.030
0.021 |
22.0-25.0
24.40 |
12.0-14.0
12.70 |
≤0.75
0.10 |
≤0.75
0.15 |
— |
≥520
610 |
≥25
37 |
用于相同类型的不锈钢及复合钢板、异种钢焊接 |
|
E310-16 |
E310-16 |
0.08-0.20
0.13 |
1.0-2.5
1.89 |
≤0.75
0.41 |
≤0.030
0.009 |
≤0.030
0.020 |
25.0-28.0
27.31 |
20.0-22.5
21.40 |
≤0.75
0.12 |
≤0.75
0.10 |
— |
≥550
650 |
≥25
34 |
焊接高温条件下工作的同类型不锈钢、异种钢的焊接，如Cr5Mo、Cr9Mo、Cr13等 |
|
E310-15 |
E310-15 |
0.08-0.20
0.14 |
1.0-2.5
1.79 |
≤0.75
0.36 |
≤0.030
0.008 |
≤0.030
0.017 |
25.0-28.0
27.46 |
20.0-22.5
21.35 |
≤0.75
0.10 |
≤0.75
0.10 |
— |
≥550
625 |
≥25
36 |
焊接高温条件下工作的同类型不锈钢及异种钢的焊接，如Cr5Mo、Cr9Mo、Cr13等 |