聚醚酰亚胺PEI ULTEM 1000
PEI 基础创新塑料(美国) 1000
透明的,标准流Polyetherimide(Tg 217 c)。符合亚州ECO,阻燃等级UL94 V0,V2和5VA。于2007年6月,这种等级将不再支持生物相容性信息,不用于医学应用需要生物相容性。替代HU1000级别。美国FDA和欧洲食品接触合规,请选择1000 F树脂。
典型的属性：
|
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress, yld, Type I, 5 mm/min |
1120 |
kgf/cm2 |
ASTM D 638 |
|
Tensile Strain, yld, Type I, 5 mm/min |
7 |
% |
ASTM D 638 |
|
Tensile Strain, brk, Type I, 5 mm/min |
60 |
% |
ASTM D 638 |
|
Tensile Modulus, 5 mm/min |
36500 |
kgf/cm2 |
ASTM D 638 |
|
Flexural Stress, yld, 2.6 mm/min, 100 mm span |
1680 |
kgf/cm2 |
ASTM D 790 |
|
Flexural Modulus, 2.6 mm/min, 100 mm span |
35800 |
kgf/cm2 |
ASTM D 790 |
|
Hardness, Rockwell M |
109 |
- |
ASTM D 785 |
|
Taber Abrasion, CS-17, 1 kg |
10 |
mg/1000cy |
ASTM D 1044 |
|
IMPACT |
Value |
Unit |
Standard |
|
Izod Impact, unnotched, 23°C |
136 |
cm-kgf/cm |
ASTM D 4812 |
|
Izod Impact, notched, 23°C |
5 |
cm-kgf/cm |
ASTM D 256 |
|
Izod Impact, Reverse Notched, 3.2 mm |
136 |
cm-kgf/cm |
ASTM D 256 |
|
Gardner, 23°C |
373 |
cm-kgf |
ASTM D 3029 |
|
THERMAL |
Value |
Unit |
Standard |
|
Vicat Softening Temp, Rate B/50 |
218 |
°C |
ASTM D 1525 |
|
HDT, 0.45 MPa, 6.4 mm, unannealed |
210 |
°C |
ASTM D 648 |
|
HDT, 1.82 MPa, 6.4 mm, unannealed |
201 |
°C |
ASTM D 648 |
|
CTE, -20°C to 150°C, flow |
5.58E-05 |
1/°C |
ASTM E 831 |
|
CTE, -20°C to 150°C, xflow |
5.4E-05 |
1/°C |
ASTM E 831 |
|
Thermal Conductivity |
0.22 |
W/m-°C |
ASTM C 177 |
|
Relative Temp Index, Elec |
170 |
°C |
UL 746B |
|
Relative Temp Index, Mech w/impact |
170 |
°C |
UL 746B |
|
Relative Temp Index, Mech w/o impact |
170 |
°C |
UL 746B |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Specific Gravity |
1.27 |
- |
ASTM D 792 |
|
Water Absorption, 24 hours |
0.25 |
% |
ASTM D 570 |
|
Water Absorption, equilibrium, 23C |
1.25 |
% |
ASTM D 570 |
|
Mold Shrinkage, flow, 3.2 mm (5) |
0.5 - 0.7 |
% |
SABIC Method |
|
Melt Flow Rate, 337°C/6.6 kgf |
9 |
g/10 min |
ASTM D 1238 |
|
ELECTRICAL |
Value |
Unit |
Standard |
|
Volume Resistivity |
1.E+17 |
Ohm-cm |
ASTM D 257 |
|
Dielectric Strength, in air, 1.6 mm |
32.7 |
kV/mm |
ASTM D 149 |
|
Dielectric Strength, in oil, 1.6 mm |
27.9 |
kV/mm |
ASTM D 149 |
|
Dielectric Strength, in oil, 3.2 mm |
19.6 |
kV/mm |
ASTM D 149 |
|
Relative Permittivity, 100 Hz |
3.15 |
- |
ASTM D 150 |
|
Relative Permittivity, 1 kHz |
3.15 |
- |
ASTM D 150 |
|
Dissipation Factor, 100 Hz |
0.0015 |
- |
ASTM D 150 |
|
Dissipation Factor, 1 kHz |
0.0012 |
- |
ASTM D 150 |
|
Dissipation Factor, 2450 MHz |
0.0025 |
- |
ASTM D 150 |
|
Arc Resistance, Tungsten {PLC} |
5 |
PLC Code |
ASTM D 495 |
|
Hot Wire Ignition {PLC) |
1 |
PLC Code |
UL 746A |
|
High Voltage Arc Track Rate {PLC} |
2 |
PLC Code |
UL 746A |
|
High Ampere Arc Ign, surface {PLC} |
3 |
PLC Code |
UL 746A |
|
Comparative Tracking Index (UL) {PLC} |
4 |
PLC Code |
UL 746A |
|
FLAME CHARACTERISTICS |
Value |
Unit |
Standard |
|
UL Recognized, 94V-2 Flame Class Rating (3) |
0.4 |
mm |
UL 94 |
|
UL Recognized, 94V-0 Flame Class Rating (3) |
0.75 |
mm |
UL 94 |
|
UL Recognized, 94-5VA Rating (3) |
3 |
mm |
UL 94 |
|
Oxygen Index (LOI) |
47 |
% |
ASTM D 2863 |
|
NBS Smoke Density, Flaming, Ds 4 min |
0.7 |
- |
ASTM E 662 |
聚醚酰亚胺PEI （Polyetherimide），PEI 是琥珀色透明固体，不添加任何添加剂PEI原料颗粒图片就有固有的阻燃性和低烟度，氧指数为47%，燃烧等级为UL94-V-0级，密度为1.28~1.42g/cm3。PEI具有很强的高温稳定性，即使是非增强型的PEI，仍具有很好的韧性和强度。因此利用PEI优越的热稳定性可用来制作高温耐热器件。具有优良的机械性能、电绝缘性能、耐辐照性能、耐高低温及耐磨性能，并可透过微波。
PEI(聚醚酰亚胺)具有优良的机械性能、电绝缘性能、耐辐照性能、耐高低温及耐磨性能，并可透过微波。PEI兼具优良的高温机械性能和耐磨性，故可用于制造输水管转向阀的阀件。由于具有很高的强度、柔韧性和耐热性，PEI是优良的涂层和成膜材料，能形成适用于电子工业的涂层和薄膜。 主要特点 连续工作温度范围大（-200--170度长期工作），玻璃化温度与热变性温度接近、熔点高达330度 在低温/高温下仍保有高机械强度、高硬度、高抗蠕变性、良好韧性 杰出的抗析出性 ( 适合用在利用蒸气消毒的杀菌室 )；不易滋生细菌，常用于食品加工业 高抗辐射性优异、可透过红外光和微波辐射；电器绝缘性好、良好的电镀性能 较宽温度（-200--170度）范围保持稳定的介电常数和损耗因数 不能通过SMT回流焊接测试 主要应用 电子行业：连接件、普通和微型继电器外壳、电路板、线圈、软性电路、反射镜、高精度密光纤元件、高温隔热板 汽车行业：连接件、高功率车灯和指示灯、控制汽车舱室外部温度的传感器、控制空气和燃料混合物温度的传感器，医 疗器材等。