ULTEM 1000F 通过FDA和NSF51认证PEI
PEI 基础创新塑料（美国） 1000F
ULTEM 1000F
聚醚酰亚胺1000 F树脂是一种无定形、透明polyetherimide(PEI)塑料，提供玻璃转变温度(Tg)217°C。这种固有的阻燃树脂UL94V0,V2和5VA评级,并通过无铅认证。聚醚酰亚胺1000 F树脂是一种无筋通用级提供耐高温、高强度和模量和广泛的化学抵抗高温。这种等级符合美国FDA和欧洲食品接触,NSF51认证。
典型属性：
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 1120 | kgf/cm2 | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 7 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 60 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 36500 | kgf/cm2 | ASTM D 638 |
| Flexural Stress, yld, 2.6 mm/min, 100 mm span | 1680 | kgf/cm2 | ASTM D 790 |
| Flexural Modulus, 2.6 mm/min, 100 mm span | 35800 | kgf/cm2 | ASTM D 790 |
| Hardness, Rockwell M | 109 | - | ASTM D 785 |
| Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | ASTM D 1044 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 136 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact, notched, 23°C | 5 | cm-kgf/cm | ASTM D 256 |
| Izod Impact, Reverse Notched, 3.2 mm | 136 | cm-kgf/cm | ASTM D 256 |
| Gardner, 23°C | 373 | cm-kgf | ASTM D 3029 |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 218 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 210 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 201 | °C | ASTM D 648 |
| CTE, -20°C to 150°C, flow | 5.58E-05 | 1/°C | ASTM E 831 |
| CTE, -20°C to 150°C, xflow | 5.4E-05 | 1/°C | ASTM E 831 |
| Thermal Conductivity | 0.22 | W/m-°C | ASTM C 177 |
| Relative Temp Index, Elec | 170 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 170 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 170 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.27 | - | ASTM D 792 |
| Water Absorption, 24 hours | 0.25 | % | ASTM D 570 |
| Water Absorption, equilibrium, 23C | 1.25 | % | ASTM D 570 |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.5 - 0.7 | % | SABIC Method |
| Melt Flow Rate, 337°C/6.6 kgf | 9 | g/10 min | ASTM D 1238 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+17 | Ohm-cm | ASTM D 257 |
| Dielectric Strength, in air, 1.6 mm | 32.7 | kV/mm | ASTM D 149 |
| Dielectric Strength, in oil, 1.6 mm | 28 | kV/mm | ASTM D 149 |
| Relative Permittivity, 1 kHz | 3.15 | - | ASTM D 150 |
| Dissipation Factor, 1 kHz | 0.0013 | - | ASTM D 150 |
| Dissipation Factor, 2450 MHz | 0.0025 | - | ASTM D 150 |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 |
| Hot Wire Ignition {PLC) | 1 | PLC Code | UL 746A |
| High Voltage Arc Track Rate {PLC} | 2 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 3 | PLC Code | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 4 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-2 Flame Class Rating (3) | 0.4 | mm | UL 94 |
| UL Recognized, 94V-0 Flame Class Rating (3) | 0.75 | mm | UL 94 |
| UL Recognized, 94-5VA Rating (3) | 3 | mm | UL 94 |
| Oxygen Index (LOI) | 47 | % | ASTM D 2863 |
| NBS Smoke Density, Flaming, Ds 4 min | 0.7 | - | ASTM E 662 |
PEI (聚醚酰亚胺)是琥珀色透明固体，不添加任何添加剂就有固有的阻燃性和低烟度，氧指数为47%，燃烧等级为UL94-V-0级，密度为1.28~1.42g/cm3。PEI具有很强的高温稳定性，即使是非增强型的PEI，仍具有很好的韧性和强度。因此利用PEI优越的热稳定性可用来制作高温耐热器件。具有优良的机械性能、电绝缘性能、耐辐照性能、耐高低温及耐磨性能，并可透过微波。PEI还有良好的阻燃性、抗化学反应以及电绝缘特性。玻璃化转化温度很高，达215℃。PEI还具有很低的收缩率及良好的等方向机械特性。加入玻璃纤维、碳纤维或其他填料可达到增强改性的目的；也可和其它工程塑料组成耐热高分子合金，可在-160～180℃的工作温度下长期使用。
聚醚亚胺树脂的长期使用温度是338T和356T（根据等级），燃烧等级达到UL94V—0（10密耳厚度。）氧指数达47，聚醚酰亚胺符合飞机内件要求的FAA阻燃性和热稀放性的材料标准。它的玻璃化转变温度为419F，并允许在392F下间断使用，在更高温度下，产生短期偏移。在356T下，拉伸温度和挠曲模量分别在41和2068MPa以上。用玻纤、碳纤维增强的材料在接近玻璃态转变温度下，具有更高的强度和刚度。
聚醚酰亚胺在高温和应力下的长期抗蠕变性允许其在许多结构设备中代替金属和其它材料。在可变温度、湿气和频率条件下表现出很好的电性能。在GHz频率下的低损耗因数使聚醚酰亚胺具有高的微波可穿性。它的离子型污染物低水准，在 250F100％ R． H．和207kPa下120小时用水提取后的导电率，在20兆欧以上，它可用作电子传感器元件的绝缘材料。
PEI是优良的涂层和成膜材料，能形成适用于电子工业的涂层和薄膜，并可用于制造孔径< 0.1μm、具有高渗透性的微孔隔膜。还可用作耐高温胶粘剂和高强度纤维等。
应用领域
由于PEI具有优良的综合平衡性能，卓有成效地应用于电子、电机和航空等工来部门，并用作传统产品和文化生活用品的金属代用材料。用PEI取代金属制造光纤连接器，可使元件结构最佳化，简化其制造和装配步骤，保持更精确的尺寸。用于汽车领域，如用以制造高温连接件、高功率车灯和指示灯、控制汽车舱室外部温度的传感器（空调温度传感器）和控制空气和燃料混合物温度的传感器（有效燃烧温度传感器）。还可用作耐高温润滑油侵蚀的真空泵叶轮、在180℃操作的蒸镏器的磨口玻璃接头（承接口）、非照明的防雾灯的反射镜。