磨砂玻璃填充PEI ULTEM 2212EPR
ULTEM ? Resin 2212EPR |
PEI 基础创新塑料（美国）2212EPR
ULTEM 2212EPR
20%磨碎的玻璃（带压花玻璃纤维）填充，增强流动Polyetherimide(Tg 217 c)与内部脱模。符合ECO，阻燃UL94-V0和5VA等级。
典型属性：
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 1090 | kgf/cm2 | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 1090 | kgf/cm2 | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 59000 | kgf/cm2 | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 1750 | kgf/cm2 | ASTM D 790 |
| Flexural Stress, brk, 2.6 mm/min, 100 mm span | 1750 | kgf/cm2 | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 56200 | kgf/cm2 | ASTM D 790 |
| Flexural Modulus, 2.6 mm/min, 100 mm span | 52000 | kgf/cm2 | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 49 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact, notched, 23°C | 5 | cm-kgf/cm | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 124 | cm-kgf | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 210 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 210 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 205 | °C | ASTM D 648 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 212 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 207 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 3.6E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 7.2E-05 | 1/°C | ASTM E 831 |
| Relative Temp Index, Elec | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 105 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.4 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.5 - 0.7 | % | SABIC Method |
| Mold Shrinkage, xflow, 3.2 mm (5) | 0.5 - 0.7 | % | SABIC Method |
| Melt Flow Rate, 337°C/6.6 kgf | 15 | g/10 min | ASTM D 1238 |
| ELECTRICAL | Value | Unit | Standard |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 |
| Hot Wire Ignition {PLC) | 1 | PLC Code | UL 746A |
| High Voltage Arc Track Rate {PLC} | 4 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 4 | PLC Code | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 4 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-0 Flame Class Rating (3) | 0.4 | mm | UL 94 |
聚醚酰亚胺PEI （Polyetherimide），PEI 是琥珀色透明固体，不添加任何添加剂PEI原料颗粒图片就有固有的阻燃性和低烟度，氧指数为47%，燃烧等级为UL94-V-0级，密度为1.28~1.42g/cm3。PEI具有很强的高温稳定性，即使是非增强型的PEI，仍具有很好的韧性和强度。因此利用PEI优越的热稳定性可用来制作高温耐热器件。具有优良的机械性能、电绝缘性能、耐辐照性能、耐高低温及耐磨性能，并可透过微波。
PEI(聚醚酰亚胺)具有优良的机械性能、电绝缘性能、耐辐照性能、耐高低温及耐磨性能，并可透过微波。PEI兼具优良的高温机械性能和耐磨性，故可用于制造输水管转向阀的阀件。由于具有很高的强度、柔韧性和耐热性，PEI是优良的涂层和成膜材料，能形成适用于电子工业的涂层和薄膜。 主要特点 连续工作温度范围大（-200--170度长期工作），玻璃化温度与热变性温度接近、熔点高达330度 在低温/高温下仍保有高机械强度、高硬度、高抗蠕变性、良好韧性 杰出的抗析出性 ( 适合用在利用蒸气消毒的杀菌室 )；不易滋生细菌，常用于食品加工业 高抗辐射性优异、可透过红外光和微波辐射；电器绝缘性好、良好的电镀性能 较宽温度（-200--170度）范围保持稳定的介电常数和损耗因数 不能通过SMT回流焊接测试 主要应用 电子行业：连接件、普通和微型继电器外壳、电路板、线圈、软性电路、反射镜、高精度密光纤元件、高温隔热板 汽车行业：连接件、高功率车灯和指示灯、控制汽车舱室外部温度的传感器、控制空气和燃料混合物温度的传感器，医 疗器材等。